PETG Filament (1kg)
High Quality & Toughness
Outstanding Performance
High Stability
High Quality & Toughness
Outstanding Performance
High Stability
Description
|
• Heat-resisting and durable, with high rigidity and flexibility |
Showcase
Fractal Pyramid
Knurling Bolt and Nut
Specifications
Weight:
1 kg
Diameter:
1.75 mm
Length:
Length: 315m / 344.49 "'
Spool Size:
200 × 65 mm / 7.87 × 2.56 "
Printing Temperature:
230 °C - 250 °C
Heated Bed Temperature:
60 °C - 80 °C
Density:
1.26 (g/cm²）
Printing Speed:
user-defined
MFR (g/10 min):
18 (230 ºC/2.16 kg) / (230 ºC/4.76 lbs.)
Tensile strength:
52 / MPa
Elongation at break:
2.5%
Bending Strength:
70 / MPa
Flexural Modulus:
2050 / MPa
HDT:
65 °C
Weight:
1 kg
Diameter:
1.75 mm
Length:
Length: 315m / 344.49 "'
Spool Size:
200 × 65 mm / 7.87 × 2.56 "
Printing Temperature:
230 °C - 250 °C
Heated Bed Temperature:
60 °C - 80 °C
Density:
1.26 (g/cm²）
Printing Speed:
user-defined
MFR (g/10 min):
18 (230 ºC/2.16 kg) / (230 ºC/4.76 lbs.)
Tensile strength:
52 / MPa
Elongation at break:
2.5%
Bending Strength:
70 / MPa
Flexural Modulus:
2050 / MPa
HDT:
65 °C
PETG Filament (1kg)
High Quality & Toughness
Outstanding Performance
High Stability
High Quality & Toughness
Outstanding Performance
High Stability
Description
|
• Heat-resisting and durable, with high rigidity and flexibility |
Showcase
Fractal Pyramid
Knurling Bolt and Nut
Specifications
Weight:
1 kg
Diameter:
1.75 mm
Length:
Length: 315m / 344.49 "'
Spool Size:
200 × 65 mm / 7.87 × 2.56 "
Printing Temperature:
230 °C - 250 °C
Heated Bed Temperature:
60 °C - 80 °C
Density:
1.26 (g/cm²）
Printing Speed:
user-defined
MFR (g/10 min):
18 (230 ºC/2.16 kg) / (230 ºC/4.76 lbs.)
Tensile strength:
52 / MPa
Elongation at break:
2.5%
Bending Strength:
70 / MPa
Flexural Modulus:
2050 / MPa
HDT:
65 °C
Weight:
1 kg
Diameter:
1.75 mm
Length:
Length: 315m / 344.49 "'
Spool Size:
200 × 65 mm / 7.87 × 2.56 "
Printing Temperature:
230 °C - 250 °C
Heated Bed Temperature:
60 °C - 80 °C
Density:
1.26 (g/cm²）
Printing Speed:
user-defined
MFR (g/10 min):
18 (230 ºC/2.16 kg) / (230 ºC/4.76 lbs.)
Tensile strength:
52 / MPa
Elongation at break:
2.5%
Bending Strength:
70 / MPa
Flexural Modulus:
2050 / MPa
HDT:
65 °C