ABS Filament (RFID) - 1kg

Name: ABS Filament (RFID) - 1kg
Brand: Snapmaker
SKU: 34237
Price: 22.99 USD
Availability: InStock

$22.99

Filament Bulk Sale: 25% OFF on 4+ rolls | 30% OFF on 6+ rolls | 35% OFF on 10+ rolls. Learn more details here.
Product Overview
• High impact resistance reduces cracking under sudden stress
• Reliable load-bearing strength for functional printed parts
• Lower brittleness supports durability through repeated use
• Improved shape retention at elevated temperatures up to 100°C

Cautions for Use
• Enclosed printing required
• Keep the filament away from direct sunlight in a sealed container with desiccant when not in use

Applicability
• 3D Printing

Printer Support & Settings:
• Snapmaker U1: Optimized profiles built into Snapmaker Orca.
• Other printers: Supports most FDM 3D printers; manual tuning may be required.

Learn More Hide

Recommendations

Filament Bulk Sale

Featured RFID Filament

As low as $17.25/roll (4+ rolls) | $16.10/roll (6+ rolls) | $14.95/roll (10+ rolls)

Payment Methods

Delivery

• CA, UK, AU, JP, KR: Ships from local warehouse · 1–2 business days dispatch · 2–7 business days delivery after dispatch
• NO, CH, IS, RS: Ships from Germany warehouse · 1–2 business days dispatch · 7–20 business days delivery after dispatch
• All other countries/regions: Ships from China warehouse · 1–2 business days dispatch · 3–10 business days delivery after dispatch

%3Cp%3EEarn%20[points_amount]%20when%20you%20buy%20this%20item.%3C/p%3E

ABS Filament (RFID) - 1kg

Snapmaker ABS

Colorful ABS filament surrounds a printed spool holder and several practical models on a tabletop.

High Impact Resistance

ABS is engineered to absorb more energy from drops, collisions, and external forces, significantly minimizing the risk of cracking or snapping under sudden stress.

Reliable Load-Bearing Performance

Engineered for reliable load-bearing performance, parts printed with this ABS filament resists embrittlement, deformation, and performance degradation under continuous loads and repeated use.

A functional ABS spool holder demonstrates load-bearing strength with six kilograms of filament.

Superior Heat Resistance

ABS has a Heat Deflection Temperature of 100℃, vastly outperforming PLA and PETG. It delivers the reliable, heat-resistant performance required for challenging applications, from high-heat automotive interiors to functional components.

A Snapmaker ABS Filament car phone holder shown before and during use on an air vent, showing the superior Heat Resistance.

Versatile Colors for Functional Creations

Snapmaker ABS filament offers a curated selection of vibrant colors to suit your diverse 3D printing needs.

ABS color range featuring green, orange, light blue, purple, yellow, white, gray, red, black, and navy blue.

RFID Recognition^[1]

When used with the Snapmaker U1, the printer automatically loads preset filament information so you don’t need to adjust settings manually, making printing easier than ever.

Recyclable Spool & Packaging

Both the spool and packing box are crafted from 100% recyclable materials, balancing eco-friendly values with superior print reliability.

Recycled-material spools hold black, green, white, blue, yellow, red, gray, orange, and purple filament.

Printing Tips

Drying & Storage

• Pre-Drying: ABS filament has low moisture sensitivity and generally does not require drying. However, pre-drying is recommended for optimal print results. The recommended setting is 80°C for 6 hours.
• Storage: When not in use, we recommend keeping the filament away from direct sunlight in a sealed container with desiccant.

Printing

• Enclosed Printing Required: This filament is sensitive to temperature fluctuations and may warp during printing. It can also produce a noticeable odor when melted, so enclosed printing is required throughout the process. For U1 printers, we recommend using the official top cover to help stabilize chamber temperature and support air filtration, addressing both issues in one setup. For better air quality, operate the printer in a well-ventilated area during printing.
• Resolving Poor Layer Adhesion: If layer bonding is insufficient, try increasing the nozzle temperature, reducing print speed, and turning off the cooling fan.
• Resolving First-Layer Warping: If first-layer warping occurs, apply glue to the build plate to improve print success. Avoid printing large models. Adding a brim can also help reduce the risk of warping.

Specifications

Recommended Printing Conditions

* Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle Temperature

240–280°C

Bed Temperature

90–100°C

Cooling Fan

OFF

Printing Speed

50–200 mm/s

Drying Settings Before Printing

80°C for 6 h

Physical Properties

Density

1.04 g/cm³ (23°C)

Melt Index

9–14 g/10 min

Glass Transition Temperature

101°C

Vicat Softening Temperature

104°C

Heat Deflection Temperature

100°C (0.45 MPa)

Saturated Water Absorption Rate

0.35%

Mechanical Properties

Tensile Strength (X-Y)

33.4 ± 0.6 MPa

Tensile Strength (Z)

29.7 ± 0.3 MPa

Breaking Elongation Rate (X-Y)

17.9 ± 1.3%

Breaking Elongation Rate (Z)

3.1 ± 0.3%

Bending Modulus (X-Y)

2127.2 ± 29.9 MPa

Bending Strength (X-Y)

56.2 ± 0.3 MPa

Impact Strength (X-Y)

18.0 ± 0.9 kJ/m² (Notched)

Recommended Printing Conditions

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle Temperature

240–260°C

Bed Temperature

60–85°C

Cooling Fan

0–60%

Printing Speed

50–150 mm/s

Drying Settings Before Printing

65°C for 6 h

Physical Properties

Density

1.30 g/cm³

Light Transmission

90%

Melt Index

11.5 g/10 min (210°C, 2.16 kg)

Glass Transition Temperature

79.2°C (10°C/min)

Vicat Softening Temperature

83.2°C

Heat Deflection Temperature

77.1°C (0.45 MPa)

Mechanical Properties

Tensile Strength (X-Y)

46 ± 1 MPa

Tensile Strength (Z)

30.99 ± 1.52 MPa

Breaking Elongation Rate (X-Y)

8.17 ± 0.98%

Breaking Elongation Rate (Z)

3.16 ± 0.6%

Bending Modulus (X-Y)

2.26 ± 0.03 GPa

Bending Modulus (Z)

1.88 ± 0.03 GPa

Bending Strength (X-Y)

72.07 ± 0.72 MPa

Bending Strength (Z)

61.24 ± 0.82 MPa

Impact Strength (X-Y)

2.91 ± 0.11 kJ/m² (Notched)
34.16 ± 1.22 kJ/m²

Impact Strength (Z)

1.09 ± 0.06 kJ/m² (Notched)
5.51 ± 0.96 kJ/m²

Downloads

Icon representing a PDF document with text lines above.

In the Box

Sealed Spool Filament × 1

Desiccant × 1

Paper Packaging Box × 1

Sealed Spool Filament × 1

Desiccant × 1

Paper Packaging Box × 1

Note:
[1] RFID function is only available for the Snapmaker U1

Frequently Asked Questions

1. Compability

• Snapmaker U1: Optimized print profiles are built into Snapmaker Orca.
• Other printers: Compatible with most FDM 3D printers. Manual parameter tuning may be required.

2. What is ABS?

ABS (Acrylonitrile Butadiene Styrene) is an engineering-grade filament known for its excellent impact resistance, heat resistance, and load-bearing performance. It is ideal for functional prototypes, mechanical parts, tooling, enclosures, and automotive interior components that require durability and long-term performance.

3. What print settings are recommended?

For the best printing results, we recommend the following settings:
• Nozzle Temperature: 240-280°C
• Bed Temperature: 90-100°C
• Print Speed: 50-200 mm/s
• Cooling Fan: Off
• Drying (if needed): 80°C for 6 hours
The recommended settings are based on a 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters.

4. Do I need to dry ABS filament before printing?

ABS filament has low moisture sensitivity and generally does not require drying. However, pre-drying is recommended for optimal print results. The recommended setting is 80°C for 6 hours.
When not in use, store the filament in a sealed container with desiccant and keep it away from direct sunlight.

5. Is a Top Cover required for ABS?

Yes. We strongly recommend using the official Top Cover when printing ABS with the Snapmaker U1.
ABS is highly sensitive to ambient temperature fluctuations and can warp, crack, or experience poor layer adhesion if printed in an open environment. It also produces a noticeable odor during printing, so proper ventilation is recommended.
The Snapmaker U1 Top Cover helps maintain a stable chamber temperature, significantly reducing the risk of warping and improving print quality. It has a three-stage air filtration system, providing a more comfortable printing experience. For the best results with ABS, the Top Cover should be installed before printing.

6. Is a Hardened Steel Hot End required for ABS?

No. A Hardened Steel Hot End is not required for printing ABS.
ABS is a non-abrasive filament and can be printed reliably with the standard Stainless Steel Hot End on the Snapmaker U1. The standard hot end fully supports the recommended printing temperatures of 240–280°C.
A Hardened Steel Hot End is generally recommended only for abrasive filaments containing materials such as carbon fiber, glass fiber, or glow-in-the-dark additives.

7. Why is my ABS print warping?

ABS has a relatively high shrinkage rate. During printing, if different parts of the model cool at different rates, uneven shrinkage creates thermal stress. When this stress exceeds the adhesion between the print and the build plate or the material's resistance to deformation, the corners may lift or the base may warp.
To reduce the risk of warping:
• Use the Top Cover to maintain a more stable chamber temperature and minimize temperature fluctuations during printing.
• Apply glue to the build plate to improve first-layer adhesion.
• Add a brim to increase the contact area with the build plate.
• Avoid printing very large ABS models when possible, as they are more susceptible to thermal stress.
• Keep the enclosure closed throughout the entire print.

Note: A closed chamber does not completely eliminate warping. Its primary purpose is to reduce temperature fluctuations during printing, which helps minimize thermal stress and significantly lowers the risk of warping.

8. Why is the layer adhesion poor?

If layer bonding is insufficient:
• Increase the nozzle temperature.
• Reduce the printing speed.
• Turn off the cooling fan.
These adjustments help improve layer bonding.

9. What applications is ABS best suited for?

ABS is ideal for durable functional parts that require strength and heat resistance, including:
• Functional prototypes
• Mechanical components
• Tooling and fixtures
• Enclosures
• Automotive interior parts
• Structural components

10. Does ABS have good heat resistance?

Yes. ABS has a Heat Deflection Temperature (HDT) of 100°C, offering better heat resistance than PLA and PETG. It is well suited for applications exposed to elevated temperatures, such as automotive interior parts and functional engineering components.

11. Can ABS be used outdoors?

ABS can be used outdoors for short-term applications. However, prolonged exposure to sunlight may cause yellowing, embrittlement, and reduced mechanical performance.
For long-term outdoor applications, ASA is recommended.

Stay Updated!

ABS Filament (RFID) - 1kg

Featured RFID Filament

Featured RFID Filament

PETG-CF Filament (RFID) - 1kg

PLA Translucent Filament (RFID) - 1kg

PLA-CF Filament (RFID) - 1kg

PETG HF Filament (RFID) - 1kg

SnapSpeed PLA Filament (RFID) - 1kg

Matte PLA Filament (RFID) - 1kg

Silk PLA Filament (RFID) - 1kg

Silk Dual-Color PLA Filament (RFID) - 1kg

PETG Translucent Filament (RFID) - 1kg

Wood PLA Filament (RFID) - 1kg

TPU 95A HF Filament (RFID) - 1kg

Snapmaker ABS

High Impact Resistance

Reliable Load-Bearing Performance

Superior Heat Resistance

Versatile Colors for Functional Creations

RFID Recognition[1]

Recyclable Spool & Packaging

Printing Tips

Specifications

Downloads

In the Box

1. Compability

2. What is ABS?

3. What print settings are recommended?

4. Do I need to dry ABS filament before printing?

5. Is a Top Cover required for ABS?

6. Is a Hardened Steel Hot End required for ABS?

7. Why is my ABS print warping?

8. Why is the layer adhesion poor?

9. What applications is ABS best suited for?

10. Does ABS have good heat resistance?

11. Can ABS be used outdoors?

ABS Filament (RFID) - 1kg

RFID Recognition^[1]