Matte PLA Filament (RFID) - 1KG

Snapmaker Matte PLA

Assorted Colors

High Speeed

Stable Performance

Snapmaker Matte PLA

Colorful 3D printed models made with Snapmaker Matte PLA Filament, showing a smooth matte finish, rich color, and reliable print quality.

Print It Matte, Keep It Classy

Delivers a soft matte finish that hides layer lines for a clean, professional look.
Ideal for art prints, decor, and sleek prototypes.

Rich Colors, Refined Tones

Color swatches in various shades arranged in a grid layout.

Color swatches displayed in a grid format with labels.

Steady Matte at High Speed

Prints at speeds up to 300mm/s with no loss in surface quality—just smooth, detailed prints every time.

Superior Print Performance

Prints at speeds up to 300mm/s with no loss in surface quality—just smooth, detailed prints every time.

Easy Support Remove

Easily separates from supports, reducing post-processing time.

Eco-Friendly and Recyclable

Made from recyclable materials, minimizing environmental impact while maintaining excellent performance.

Specifications

RECOMMENDED PRINTING CONDITIONS

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

190–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

190-300 mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.31g/cm³ at 23°C

Melt index

14–20 g/10min

THERMAL PROPERTIES

Glass transition temperature

60.6°C

Melting temperature

162.6°C

Vicat softening temperature

62.7°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

57.8°C

MECHANICAL PROPERTIES

Young's modulus (X-Y)

1997±64 MPa

Young's modulus (Z)

1615±54 MPa

Tensile strength (X-Y)

23.2±0.5 MPa

Tensile strength (Z)

12.2±0.7 MPa

Elongation at break

27.8±2.4%

Elongation at break (Z)

0.9±0.1%

Bending modulus (X-Y)

2209±75 MPa

Bending strength (X-Y)

40.4±1.1 MPa

Charpy impact strength (X-Y)

6.7±0.5kJ/㎡

RECOMMENDED PRINTING CONDITIONS

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

190–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

190-300 mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.31g/cm³ at 23°C

Melt index

14–20 g/10min

THERMAL PROPERTIES

Glass transition temperature

60.6°C

Melting temperature

162.6°C

Vicat softening temperature

62.7°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

57.8°C

MECHANICAL PROPERTIES

Young's modulus (X-Y)

1997±64 MPa

Young's modulus (Z)

1615±54 MPa

Tensile strength (X-Y)

23.2±0.5 MPa

Tensile strength (Z)

12.2±0.7 MPa

Elongation at break

27.8±2.4%

Elongation at break (Z)

0.9±0.1%

Bending modulus (X-Y)

2209±75 MPa

Bending strength (X-Y)

40.4±1.1 MPa

Charpy impact strength (X-Y)

6.7±0.5kJ/㎡